Thermal Barrier Coating Life Prediction Model Development

By: Nasa, National Aeronautics and Space Adm

This report describes work performed to determine the predominat modes of degradation of a plasma sprayed thermal barrier coating system and to develop and verify life prediction models accounting for these degradation modes. The primary TBC system consisted of a low pressure plasma sprayed NiCrAlY bond coat, an air plasma sprayed ZrO2-Y2O3 top coat, and a Rene' 80 substrate. The work was divided into 3 technical tasks. The primary failure mode to be addressed was loss of the zirconia layer through spalling. Experiments showed that oxidation of the bond coat is a significant contributor to coating failure. It was evident from the test results that the species of oxide scale initially formed on the bond coat plays a role in coating degradation and failure. It was also shown that elevated temperature creep of the bond coat plays a role in coating failure. An empirical model was developed for predicting the test life of specimens with selected coating, specimen, and test condition variations. In the second task, a coating life prediction model was developed based on the data from Task 1 experiments, results from thermomechanical experiments performed as part of Task 2, and finite element analyses of the TBC system during thermal cycles. The third and final task attempted to verify the validity of the model developed in Task 2. This was done by using the model to predict the test lives of several coating variations and specimen geometries, then comparing these predicted lives to experimentally determined test lives. It was found that the model correctly predicts trends, but that additional refinement is needed to accurately predict coating life. Hillery, R. V. and Pilsner, B. H. and Mcknight, R. L. and Cook, T. S. and Hartle, M. S. LIFE (DURABILITY); PREDICTIONS; THERMAL CONTROL COATINGS; ALUMINUM; CHROMIUM; DEGRADATION; FAILURE MODES; NICKEL; PLASMA SPRAYING; SUBSTRATES; YTTRIUM; ZIRCONIUM...

• Format: Paperback
• Language: English
• ISBN: 1731489056
• ISBN13: 9781731489050
• Release Date: January 1
• Publisher: Independently Published
• Length: 160 Pages
• Weight: 0.85 lbs.
• Dimensions: 0.3" x 8.5" x 11.0"