Friction and Wear Behavior of Single-Crystal Silicon Carbide in Contact with Titanium

By: Nasa, National Aeronautics and Space Adm

Sliding friction experiments were conducted with single crystal silicon carbide in sliding contact with titanium. Results indicate that the friction coefficient is greater in vacuum than in argon and that this is due to the greater adhesion or adhesive transfer in vacuum. Thin films of silicon carbide transferred to titanium also adhered to silicon carbide both in argon at atmospheric pressure and in high vacuum. Cohesive bonds fractured on both the silicon carbide and titanium surfaces. The wear debris of silicon carbide created by fracture plowed the silicon carbide surface in a plastic manner. The friction characteristics of titanium in contact with silicon carbide were sensitive to the surface roughness of silicon carbide, and the friction coefficients were higher for a rough surface of silicon carbide than for a smooth one. The difference in friction results was due to plastic deformation (plowing of titanium). Miyoshi, K. and Buckley, D. H. Glenn Research Center NASA-TP-1035, E-9067 RTOP 506-16

• Format: Paperback
• Language: English
• ISBN: 1719957126
• ISBN13: 9781719957120
• Release Date: January 1
• Publisher: Independently Published
• Length: 28 Pages
• Weight: 0.20 lbs.
• Dimensions: 0.1" x 8.5" x 11.0"